Başlık Levhalı Kaynaklı Birleşim Tasarımı

a ≥ a _min     

a

6 mm

√

a _min

4 mm

Tablo 13.4

√

a ≥ a _min     

a

6 mm

√

a _min

3.5 mm

Tablo 13.4

√

a ≥ a _min     

a

6 mm

√

a _min

3.5 mm

Tablo 13.4

√

a ≥ a _min     

a

6 mm

√

a _min

4 mm

Tablo 13.4

√

a ≥ a _min     

a

6 mm

√

a _min

4 mm

Tablo 13.4

√

L_wı

520 mm

L_wt

280 mm

F_e

490 N/mm²

R_nwl

R_nwt

R_nw

w

8.487 mm

F_u-plate

410 N/mm²

F_{u flange}

410 N/mm²

t_p

16 mm

t_f

18 mm

R_nBM

R_n

ΦR_n

143.884 kN

1140.426 kN

0.126

√

A_g

F_y

275 N/mm²

R_n

ÇYTHYEDY 13.15

ΦR_n

143.884 kN

1108.8 kN

0.130

√

A_n

A_e

F_u

410 N/mm²

U

1.00

R_n

ÇYTHYEDY 13.16

ΦR_n

143.884 kN

1377.6 kN

0.104

√

A_g

A_nv

A_nt

F_y

275 N/mm²

F_u

410 N/mm²

U_bs

1

R_n

ÇYTHYEDY 13.19

ΦR_n

143.884 kN

1269 kN

0.113

√

K

0.65

L

20 mm

r

4.619 mm

KL/r

2.81

F_y

275 N/mm²

A_g

R_n

ÇYTHYEDY 13.20

(KL/r<25)

ΦR_n

143.884 kN

1108.8 kN

0.130

√

w

8.487 mm

F_E

490 N/mm²

l

260 mm

e

117.5 mm

R_n

ΦR_n

15.529 kN

374.02 kN

0.042

√

Fe

490000 kN/m²

w

Birleşim menüsünden alınan kaynak kalınlığı 0.707*w değeridir.  6/0.707=8.487 mm

Fu

410  N/mm²

t

10 mm

R_nw

R_nBM

Rn

ΦR_n

66.153 kN/m

1323 kN/m

0.042

√

A_g

F_y

275 N/mm²

R_n

ÇYTHYEDY 13.17

ΦR_n

15.529 kN

429 kN

0.036

√

A_nv

F_u

410 N/mm²

R_n

ÇYTHYEDY 13.18

ΦR_n

15.529 kN

376.38 kN

0.041

√

d_p

260 mm

F_y

275 N/mm²

t_p

10 mm

a

117.5 mm

R_n

ΦR_n

15.529 kN

273.948 kN

0.057

√

P_r

1621.397 kN

ÇYTHYEDY 13.29a

P_y

F_y

275000 kN/m²

A_g

28634.759 mm²

d_c

650 mm

t_w

16 mm

R_n

ΦR_n

103.141 kN

1544.4 kN

0.067

√